Conclusions Studies of corundum and aluminosilicate refractories of dense and granular structures in an atmosphere of hydrogen and dissociated ammonia at 1200, 1500, and 1700°C in periods of 175 and 50 h showed that the resistance of the products increases with an increase in the alumina concentration and density. The maximum resistance is exhibited by corundum products. In the aluminosilicate refractories there is some additional sintering of the material with the separation of mullite and glass. Simultaneously on the surface of the specimens we detected deeper mineralogical changes, accompanied by the decomposition of the mullite, with the formation of corundum, silicon monoxide, and glass. The changes in the phase composition are accompanied by a change in the structure, and an increase in the creep. Considering that a reduction in the temperature of 100°C causes a reduction in the creep by approximately a half [26], it can be recommended that corundum refractories should be used (under a load of 2 kg/cm2) in a reducing atmosphere at temperatures of up to 1550–1600°C, sillimanite up to 1450–1500°C, kaolin and chamotte (high-grog) up to 1300°C, with a reduction in the load and an increase in the density, the temperature of application for the products examined, especially corundum, can be increased.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1007/BF01284840
Permalink