Description:
In an attempt to enhance the electrical and mechanical properties of the high temperature superconducting oxides, high T(sub c) composites were prepared composed of the 123 compounds and AgO. The presence of extra oxygen due to the decomposition of AgO at high temperature is found to stabilize the superconducting 123 phase. Ag is found to serve as clean flux for grain growth and precipitates as pinning center. Consequently, almost two orders of magnitude enhancement in critical current densities were also observed in these composites. In addition, these composites also show much improvement in workability and shape formation. On the other hand, proper oxygen treatment of Y5Ba6Cu11Oy was found to possibly stabilize superconducting phase with T(sub c) near 250 K. I-V, ac susceptibility, and electrical resistivity measurements indicate the existence of this ultra high T(sub c) phase in this compound. Detailed structure, microstructure, electrical, magnetic and thermal studies of the superconducting composites and the ultra high T(sub c) compound are presented and discussed.
Keywords:
SOLID-STATE PHYSICS
Type:
NASA, Goddard Space Flight Center, AMSAHTS 1990: Advances in Materials Science and Applications of High Temperature Superconductors; p 8
Format:
application/pdf
Permalink