ALBERT

Description: A series of experiments performed using the Pore Formation and Mobility Investigation (PFMI) apparatus within the glovebox facility (GBX) on board the International Space Station (ISS) has provided video images of the morphological evolution of a three-dimensional interface in a diffusion controlled regime. The experimental samples were prepared on ground by filling glass tubes, 1 cm ID and approximately 30 cm in length, with "alloys" of succinonitrile (SCN) and water in an atmosphere of nitrogen at 450 millibar pressure. The compositions of the samples processed and analyzed are 0.25,0.5 and 1.0 wt% water. Experimental processing parameters of temperature gradient and translation speed, as well as camera settings, were remotely monitored and manipulated from the ground Telescience Center (TSC) at the Marshall !3pace Flight Center. During the experiments, the sample was first subjected to a unidirectional melt back, generally at 10 microns per second, with a constant temperature gradient ahead of the melting interface. Following the melt back, the interface was allowed to stabilize before translation is initiated. The temperatures in the sample were monitored by six in situ thermocouples and the position is monitored by an optical linear encoder. For the experiments performed and analyzed, the gradients ranged from 2.5 - 3.3 K/mm and the initial pulling velocities ranged from 0.7 micron per second to 1 micron per second with subsequent transition velocities of up to 100 microns per second. The data provided by the PFMI for analysis includes near-real-time (NRT) video captured on the ground during the experiment runs, ISS Video Tape Recorder (VTR) data dumped from the VTR at the end of the experiment run and recorded on the ground, telemetry data including temperature and position measurements, and limited flight HI-8 tapes in 2 camera views of experiment runs for which tapes have been returned to the investigators from ISS. Because of limited down mass from the ISS, the majority of the initial analysis has been performed using the NRT and VTR video data but will be supplemented with the HI-8 video as it becomes available. hardware and procedures required to prepare samples for correlation to flight samples is described. Using this ground-based system, a series of experiments have been performed for direct comparison with the flight data. The results of these comparisons as well as implications to future microgravity experiments are presented and discussed. A ground-based thin-sample directional solidification system as well as all associated