Publication Date:
2019-07-18
Description:
We demonstrate the possibility of making conductive and dry adhesive interfaces between multiwalled carbon nanotube (MWNT) and nanofiber (MWNF) arrays grown by chemical vapor deposition with transition-metal as catalyst on highly Boron doped silicon substrates. The maximum observed adhesion force between MWNT and MWNF surfaces is 3.5 mN for an apparent contact area of 2 mm by 4 mm. The minimum contact resistance measured at the same time is approx.20 Omega. Contact resistances of MWNT-MWNT and MWNT-gold interfaces were also measured as pressure forces around several mN were applied at the interface. The resulting minimum contact resistances are on the same order but with considerable variation from sample to sample. For MWNT-MWNT contacts, a minimum contact resistance of approx.1 Omega is observed for a contact area of 2 mm by 1 mm. The relatively high contact resistances, considering the area density of the nanotubes, might be explained by the high cross-tube resistances at the contact interfaces.
Keywords:
Mechanical Engineering
Type:
ASME Integrated Nanosystems Conference; Sep 22, 2004; Pasadena, CA; United States
Format:
text
Permalink