ALBERT

Description: The use of the activated carbon produced from rice hulls to control NOx emissions for future deep space missions has been demonstrated. The optimal carbonization temperature range was found to be between 600 and 750 degrees C. A burnoff of 61.8% was found at 700 degrees C in pyrolysis and 750 degrees C in activation. The BET surface area of the activated carbon from rice hulls was determined to be 172 m2/g when prepared at 700 degrees C. The presence of oxygen in flue gas is essential for effective adsorption of NO by activated carbon. On the contrary, water vapor inhibits the adsorption efficiency of NO. Consequently, water vapor in flue gas should be removed by drying agents before adsorption to ensure high NO adsorption efficiency. All of the NO in the flue gas was removed for more than 1.5 h when 10% oxygen was present and the ratio of the carbon weight to the flue gas flow rate (W/F) was 15.4 g min/L. Reduction of the adsorbed NO to form N2 could be effectively accomplished under anaerobic conditions at 550 degrees C. The adsorption capacity of NO on the activated carbon was found to be 5.02 mg of NO/g of carbon. The loss of carbon mass was determined to be about 0.16% of the activated carbon per cycle of regeneration if the regeneration occurred when the NO in the flue gas after the carbon bed reached 4.8 ppm, the space maximum allowable concentration. The reduction of the adsorbed NO also regenerated the activated carbon, and the regenerated activated carbon exhibited an improved NO adsorption efficiency.

Description: The wheat straw, an inedible biomass that can be continuously produced in a space vehicle has been used to produce activated carbon for effective control of NOx emissions from the incineration of wastes. The optimal carbonization temperature of wheat straw was found to be around 600 degrees C when a burnoff of 67% was observed. The BET surface area of the activated carbon produced from the wheat straw reached as high as 300 m2/g. The presence of oxygen in flue gas is essential for effective adsorption of NO by activated carbon. On the contrary, water vapor inhibits the adsorption efficiency of NO. Consequently, water vapor in flue gas should be removed by drying agents before adsorption to ensure high NO adsorption efficiency. All of the NO in the flue gas was removed for more than 2 h by the activated carbons when 10% oxygen was present and the ratio of carbon weight to the flue gas flow rate (W/F) was 30 g min/L, with a contact time of 10.2 s. All of NO was reduced to N2 by the activated carbon at 450 degrees C with a W/F ratio of 15 g min/L and a contact time of 5.1 s. Reduction of the adsorbed NO also regenerated the activated carbon, and the regenerated activated carbon exhibited an improved NO adsorption efficiency. However, the reduction of the adsorbed NO resulted in a loss of carbon which was determined to be about 0.99% of the activated carbon per cycle of regeneration. The sufficiency of the amount of wheat straw in providing the activated carbon based on a six-person crew, such as the mission planned for Mars, has been determined. This novel approach for the control of NOx emissions is sustainable in a closed system such as the case in space travel. It is simple to operate and is functional under microgravity environment.

Description: This paper presents the results from a joint research initiative between NASA Ames Research Center and Lawrence Berkeley National lab. The objective of the research is to produce activated carbon from life support wastes and to use the activated carbon to adsorb and chemically reduce the NO(sub x) and SO(sub 2) contained in incinerator flue gas. Inedible biomass waste from food production is the primary waste considered for conversion to activated carbon. Results to date show adsorption of both NO(sub x) and SO(sub 2) in activated carbon made from biomass. Conversion of adsorbed NO(sub x) to nitrogen has also been observed.