The protective value of the top layers formed in alkali-hydrogen fluorides on soft steelBy means of solubility and elastic corrosion tests, extended over lengthy testing periods, in mineral acids of different degrees of concentration, investigations were carried out on the protective value of the top layers formed on mild steel in different alkali-hydrogen-fluoride solutions (KF, HF, (NH4)F, HF, hydrogen fluoride mixture). Both methods yielded, by and large, identical results. They showed that the mean corrosion rate of soft steel pre-treated in alkali-hydrogen-fluoride solutions amounted to no more than about 10 to 15 per cent. of that of the unprotected metal so that the top layer can be said to have a protective value of 85 to 90 per cent.
Notizen:
Untersucht wurde der Schutzwert von in verschiedenen Alkalihydrogenfluorid-Lösungen (KF, HF-, (NH4)F, HF-, Hydrogenfluorid-Gemisch) auf Weichstahl gebildeten Schutzschichten im Vergleich zu dem Verhalten von ungeschütztem Weichstahl durch Löslichkeits - und Federungs-Korrosionsversuche in Mineralsäuren unterschiedlicher Konzentration über längere Versuchszeiten. Beide Methoden ergaben weitgehend das gleiche Bild. Danach beträgt die mittlere Korrosions-geschwindigkeit von in Alkalihydrogen-fluorid-Lösungen vorbehandeltem Weichstahl nur etwa 10 bis 15% von dem des ungeschützten Materials, was einem Schutzwert der Deckschicht von 85 bis 90% gleichkommt.
Zusätzliches Material:
11 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/maco.19630140802
Permalink