rigid-rod polymer
;
cation
;
dialysis
;
molecular weight
;
cast
;
aggregated
;
isotropic
;
anisotropic
;
film
;
depletion measurement
;
ionic conductivity
;
x-ray scattering
;
Chemistry
;
Polymer and Materials Science
Quelle:
Wiley InterScience Backfile Collection 1832-2000
Thema:
Chemie und Pharmazie
,
Physik
Notizen:
Poly[(1,7-dihydrobenzo[1,2-d:4,5-d′] diimidazole-2,6-diyl)-2-(2-sulfo)-p-phenylene], a conjugated rigid-rod polymer, was derivatized with pendants of propane-sulfonated ionomers. The derivatized rigid-rod polymer was soluble in aprotic solvents as well as in water for isotropic solutions that were processed into isotropic films. Direct-current electrical conductivity σ of the films was measured using the four-probe technique. Room-temperature σ as high as 2.9 × 10-4S/cm was achieved on pristine isotropic films without using dopants. When the rigid-rod polymer concentration exceeded 25 wt %, the isotropic solution could be transformed into a liquid-crystalline solution that allowed deformations to be applied to produce anisotropic films. Significant increase in σ was obtained in a sheared film along both the parallel direction (∥) and the transverse direction (⊥) with a σ∥/σ⊥ = 5. Additionally, enhanced σ was realized in films heat-treated at about 100°C, in the derivatized polymer with higher molecular weight from dialysis, and in substituting the sulfonated ion Na+ by H+ in the pendants of the polymers. Constant-voltage measurements were applied to the polymers to monitor the σ stability for ascertaining the nature of the conductivity. No electronic contribution in σ was detected. Instead, a monotonically decreasing σ was consistently observed indicative of ionic conductivity. © 1993 John Wiley & Sons, Inc.
Zusätzliches Material:
6 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/polb.1993.090311306
Permalink