Pt-Pd/alumina
;
combustion catalyst
;
hydrothermal treatment
;
xylene oxidation
;
light-off temperature
;
TEM/STEM/EDS
;
LEIS
Source:
Springer Online Journal Archives 1860-2000
Topics:
Chemistry and Pharmacology
Notes:
Abstract Two Pt/Pd catalysts on cordierite monoliths were prepared by impregnating two differently treated alumina washcoats with 10 μmol [Pt+Pd] per gram catalyst in the atomic ratio Pt/Pd=4.0. Both washcoats were first thermally treated, calcined, for 2 h at 550 °C in air and one of them was additionally treated, hydrothermally, in 100% steam for 2 h at 814 °C. The hydrothermally treated catalyst was more active for complete oxidation of xylene in air: its light-off temperature was 232 °C, compared to 259 °C for the sample calcined only. To explain this higher activity, both catalysts were characterized by BET surface area, pore-size distribution, hydrogen chemisorption, X-ray diffraction, TEM/STEM/EDS and low-energy ion scattering spectroscopy (LEIS). The catalyst with a hydrothermally treated washcoat had 30% lower surface area, larger alumina crystal size, higher degree of crystallization of alumina and larger average catalyst pore size (11 nm vs. 6 nm), than the one with the washcoat, treated only thermally. The LEIS results indicated a surface enrichment of Pd on both catalysts. The Pt signal in LEIS was higher for the hydrothermally treated sample.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF00770944
Permalink