Several important aspects of the flow in polymer melts through capillaries remain unexplored. This paper examines experimentally one such effect associated with the radial shear-stress gradient in capillaries. During capillary melt flow of a polymer with a wide molecular weight distribution, migration of the large molecules away from the region of highest shear stress, i.e., at the capillary wall, has been predicted but only modestly investigated. This effect has the potential to produce a molecular weight spectrum over the cross section of extruded polymer. Studies of distribution in shear were conducted on a well-characterized wide-distribution polystyrene (M̄w = 234,000). An Instron Rheometer equipped with a long capillary (length/diameter ratio of 66.7) was used to perform the extrusion at temperatures of 160-250°C. A solvent coring procedure was used to dissolve away concentric layers of polymer from the extrudate for molecular weight analyses. The method has been shown to cut clean sections without selective extraction. Values of M̄w, M̄n and M̄w/M̄n were calculated from complete molecular weight distribution data obtained by calibrated gel permeation chromatography. For a wide range of shear rates and temperatures, no evidence for molecular fractionation was observed. Shear degradation of this polymer was found to be small. However, at high shear rates at 250°C, evidence indicating extensive shear-induced thermal degradation was found. No evidence for oxidative degradation at the extrudate surface was found at either low or high shear rates at this temperature.
Zusätzliches Material:
2 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/pol.1972.160100509
Permalink