ALBERT

Description: Fe(II) bearing iron (oxyhydr)oxides were directly co-precipitated with Np(V)O2+ under anaerobic conditions to form Np doped magnetite and green rust. These environmentally relevant mineral phases were then characterised using geochemical and spectroscopic analyses. The Np doped mineral phases were then oxidised in air over 224 days with solution chemistry and end-point oxidation solid samples collected for further characterisation. Analysis using chemical extractions and X-ray absorption spectroscopy (XAS) techniques confirmed that Np(V) was initially reduced to Np(IV) during co-precipitation of both magnetite and green rust. Extended X-Ray Absorption Fine Structure (EXAFS) modelling suggested the Np(IV) formed a bidentate binuclear sorption complex to both minerals. Furthermore, following oxidation in air over several months, the sorbed Np(IV) was partially oxidised to Np(V), but very little remobilisation to solution occurred during oxidation. Here, linear combination fitting of the X-Ray Absorption Near Edge Structure (XANES) for the end-point oxidation samples for both mineral phases suggested approximately 50% oxidation to Np(V) had occurred over 7 months of oxidation in air. Both the reduction of Np(V) to Np(IV) and inner sphere sorption in association with iron (oxyhydr)oxides, and the strong retention of Np(IV) and Np(V) species with these phases under robust oxidation conditions, have important implications in understanding the mobility of neptunium in a range of engineered and natural environments.

Description: One of the most challenging components of the UK nuclear legacy is Magnox sludge, arising from the corrosion of Mg alloy-clad irradiated metallic U fuel that has been stored in high pH ponds. The sludges mainly comprise Mg hydroxide and carbonate phases, contaminated with fission products and actinides, including Pu. Cementation and deep geological disposal is one option for the long-term management of this material, but there is a need to understand how Pu may be leached from the waste, if it is exposed to groundwater. Here, we show that cemented Mg(OH)2 powder prepared with Pu(IV)aq is altered on contact with water to produce a visibly altered ‘leached zone’, which penetrates several hundred microns into the sample. In turn, this zone shows slow leaching of Pu, with long-term leaching rates between 1.8–4.4 × 10−5% of total Pu per day. Synchrotron micro-focus X-ray fluorescence mapping identified decreased Pu concentration within the ‘leached zone’. A comparison of micro-focus X-ray absorption spectroscopy (µ-XAS) spectra collected across both leached and unleached samples showed little variation, and indicated that Pu was present in a similar oxidation state and coordination environment. Fitting of the XANES spectra between single oxidation state standards and EXAFS modeling showed that Pu was present as a mixture of Pu(IV) and Pu(V). The change in Pu oxidation from the stock solution suggests that partial Pu oxidation occurred during sample ageing. Similarity in the XAS spectra from all samples, with different local chemistries, indicated that the Pu oxidation state was not perturbed by macro-scale variations in cement chemistry, surface oxidation, sample aging, or the leaching treatment. These experiments have demonstrated the potential for leaching of Pu from cementitious waste forms, and its underlying significance requires further investigation.