ALBERT

Description: Dark brown molecular film deposits were found at numerous locations on the Long Duration Exposure Facility (LDEF) and have been documented in great detail by several investigators. The exact deposition mechanism for these deposits is as yet unknown, although direct and scattered atomic oxygen, and solar radiation interacting with materials outgassing products have all been implicated in the formation process. Specimens of the brown molecular film were taken from below the flange of the experimental tray located at position D10 on the LDEF. The tray was one of two, comprising the same experiment, the other being located on the wake facing side of the LDEF satellite at position B4. Having access to both trays, we were able to directly compare the effect that orientation with respect to the atomic oxygen flux vector had on the formation of the brown molecular film deposits. The film is thickest on surfaces facing toward the exterior, i.e. the tray corner, as can be seen by comparing the lee and wake aspects of the rivets. The patterns appear to be aligned not with the velocity vector but with the corner of the tray suggesting that flux to the surface is due to scattered atomic oxygen rather than direct ram impingement. The role of scattered flux is further supported by more faint plume patterns on the sides of the tray. The angle of these plumes is strongly aligned with the ram direction but the outline of the deposit implies that incident atoms are scattered by collisions with the edges of the opening resulting in a directed, but diffuse, flux of atomic oxygen to the surface. Spectral reflectance measurements in the 2 to 10 micron (4000 to 1000 wavenumbers) spectral range are presented for the film in the 'as deposited' condition and for the free standing film. The material was analyzed by FTIR (Fourier Transform Infrared) microspectroscopy using gold as the reference standard. The 'as deposited' specimen was on an aluminum rivet taken from beneath the tray flange while the free film was obtained by chipping some of the material from the rivet. The transmission spectrum over the 2 to 10 micron range for the free film is presented. This spectrum appears to be essentially the same as that presented by Crutcher et.al. for films formed at vent sites which faced into the ram direction and suggested to originate from urethanes and silicones used on the LDEF. Banks et. al. state that silicones, when exposed to atomic oxygen, release polymeric scission fragments which deposit on surfaces and form a glassy, dark contaminant layer upon further atomic oxygen exposure and solar irradiation.

Description: The so called 'nicotine stain' documented at many locations on the Long Duration Exposure Facility is still unexplained as to the exact origin and mechanism of deposition, although enough is known to have some understanding of the conditions coincident for the formation of the deposits. Direct and scattered atomic oxygen flux, and solar ultraviolet radiation interacting with materials outgassing products have all been implicated in the formation of the dark brown contamination deposits. The nicotine stain represents a potential of performance degradation for spacecraft designed for long term operation in low Earth orbit and therefore, a need exists to characterize this form of spacecraft self contamination and quantify the impact on thermal/optical systems. Optical property measurements in the spectral range of 2 to 10 microns were performed on specimens of the contaminated film. Reflectance measurements of the contaminant film as deposited on the surface and as free standing films are presented along with transmission spectra for the bulk material. Thickness measurements along with micrographic examination of the cross section of the deposit reveal the layered structure of the deposit which further implicates solar illumination as a factor in the deposition mechanism.