ISSN:
1573-8663
Keywords:
ferroelectric thin films
;
(Ba,Sr)TiO3
;
pulsed laser deposition
;
microwave dielectrics
;
loss tangent
;
strain
Source:
Springer Online Journal Archives 1860-2000
Topics:
Electrical Engineering, Measurement and Control Technology
,
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Notes:
Abstract Single phase, (1 0 0) epitaxial Ba0.5Sr0.5TiO3 (BST) films have been deposited onto (1 0 0) LaAlO3 and MgO substrates by pulsed laser deposition (PLD). The capacitance and dielectric losses of as-deposited and annealed films have been measured from 1–20 GHz as a function of electric field (0–80 kV/cm) at room temperature. The dielectric properties are strongly affected by the substrate type, post-deposition annealing time (≤6 h) and temperature (≤1200°C). For epitaxial BST films deposited onto MgO, it is observed that, after a post-deposition anneal the dielectric constant and the dielectric loss decreases. For epitaxial BST films deposited onto LAO, a post-deposition anneal (≤1000°C) results in an increase in the dielectric constant and an increase in the dielectric loss. The dc electric field induced change in the dielectric constant tends to increase with the dielectric constant and is largest for as-deposited films on MgO and post-deposited annealed films on LAO. In general, for epitaxial BST films, a large electric field effect is observed in films that have a large dielectric loss and a small electric field effect in films that have a low dielectric loss. High resolution X-ray diffraction measurements indicate that deposited film exhibit a significant tetragonal distortion which is strongly affected by a by a post deposition anneal. The observed differences in dielectric properties of the epitaxial BST films on MgO and LAO are attributed to the differences in film stress which arise as a consequence of the lattice mismatch between the film and the substrate and the differences in the thermal coefficient of expansion between the film and the substrate. A thin amorphous buffer layer of BST has been used to relieve stress induced by the lattice mismatch between the film and the substrate. Unlike epitaxial films, stress relieved films do not show an inverse relationship between dielectric tuning and Q (1/tanδ) and may be superior materials for tunable microwave devices.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1023/A:1009974929096
Permalink