Simultaneous synthesis and sintering of hexagonal α-Ti1−x-Alx(N) (0 ≤x≤ 0.08) solid solutions, which contain a small amount of nitrogen, have been performed by a self-propagating high-temperature combustion method under a nitrogen pressure of 4 MPa. Dense materials (∼99% of theoretical) prepared directly from a mixture of elemental (Ti and Al) powders reveal homogeneous microstructure composed of fine grains (12–16 μm). α-Ti1−xAlx(N) (x= 0.02; Ti0.98Al0.02N0.26) exhibits a three-point bending strength σb of 390 MPa, a Vickers hardness Hv of 9.24 GPa, and a fracture toughness KIC of 4.89 MPa·m1/2; their mechanical properties are much improved by doping Al into α-Ti(N), in comparison with those (σb= 245 MPa, Hv= 9.02 GPa, and KIC= 3.77 MPa·m1/2) of α-Ti(N) fabricated under the same conditions.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1111/j.1151-2916.2004.tb06357.x
Permalink