Publication Date:
2011-08-18
Description:
CdS films have been prepared by spraying in air solutions of thiourea with either cadmium chloride or cadmium acetate with varying mole ratio and substrate temperature, and subsequently heat treating in oxygen. Substrates included both bare glass or sapphire and transparent conducting oxide-coated sapphire for electrical measurements lateral and transverse to the CdS plane, respectively. Dark resistances of over 10 to the 14th ohms and light-to-dark conductivities of up to 10 to the 7th were obtained using uncoated substrates. The use of Cd(C2H3O2)2 in place of CdCl2 greatly increased the speed of response although with some sacrifice in photoconductivity. Deposition of CdS on ITO-coated surfaces led to greatly reduced dark resistances for the case of CdCl2, but not Cd(C2H3O2)2, presumably due to HCl reaction with the ITO coating in the course of spraying with the former. Ion microprobe analysis detected indium within the CdS films exhibiting low dark resistance. Measurements of the dark and light conductivities at temperatures down to 77 K are given as are the response times for unetched and HCl-etched surfaces.
Keywords:
SOLID-STATE PHYSICS
Type:
Journal of Vacuum Science and Technology A (ISSN 0734-2101); 2; 332-335
Format:
text
Permalink