Thermophysical properties between 293 and 1863 K were investigated for laser-sintered Zr–ZrB 2 cermets containing 30, 50, and 70 wt% Zr. The measured values of coefficient of thermal expansion of Zr–ZrB 2 cermets were larger than the predicted values due to the effect of Zr–O solid solution, which was formed during laser sintering. The order–disorder phase transition of Zr–O solid solution resulted in the sharp increase in heat capacity between 625 and 675 K. Thermal conductivities were calculated from measured densities, heat capacities, and thermal diffusivities. Thermal diffusivities at 473 K were 14.0, 12.2, and 8.0 mm 2 /s for 30Zr–ZrB 2 , 50Zr–ZrB 2 , and 70Zr–ZrB 2 , respectively. Thermal conductivities at 473 K were 38, 31, and 20 W·(m·K) −1 for 30Zr–ZrB 2 , 50Zr–ZrB 2 , and 70Zr–ZrB 2 , respectively. Electron contribution to thermal conductivity of the 70Zr–ZrB 2 cermet was determined using electrical resistivity measurements, which shows that total thermal conductivity mostly came from the electron contribution at high temperatures (1073–1473 K) while the phonon contribution was very small.
Print ISSN:
0002-7820
Digitale ISSN:
1551-2916
Thema:
Maschinenbau
Permalink