Description: This paper reviews the strategies that have been reported in the literature to attempt to reinforce glass-ionomer dental cements, both conventional and resin-modified. These cements are widely used in current clinical practice, but their use is limited to regions where loading is not high. Reinforcement might extend these applications, particularly to the posterior dentition. A variety of strategies have been identified, including the use of fibres, nanoparticles, and larger particle additives. One problem revealed by the literature survey is the limited extent to which researchers have used International Standard test methods. This makes comparison of results very difficult. However, it does seem possible to draw conclusions from this substantial body of work and these are (1) that powders with conventional particle sizes do not reinforce glass-ionomer cements, (2) certain fibres and certain nanoparticles give distinct improvements in strength, and (3) in the case of the nanoparticles these improvements are associated with differences in the morphology of the cement matrix, in particular, a reduction in the porosity. Despite these improvements, none of the developments has yet been translated into clinical use.

Description: The aim of the study was to evaluate the effects of incorporation of Al2O3, ZrO2 and TiO2 nanoparticles into glass–ionomer cements (GICs). Two different GICs were used in the study. Four groups were prepared for each material: the control group (without nanoparticles) and three groups modified by the incorporation of nanoparticles at 2, 5 or 10 wt %, respectively. Cements were mixed and placed in moulds (4 mm × 6 mm); after setting, the samples were stored in saline (one day and one week). Compressive strengths were measured and the morphology of the fractured surfaces was analyzed by scanning electron microscopy. The elements released into the storage solutions were determined by Inductively coupled plasma-optical emission spectrometry (ICP-OES). Addition of nanoparticles was found to alter the appearance of cements as examined by scanning electron microscopy. Compressive strength increased with the addition of ZrO2 and especially TiO2 nanoparticles, whereas the addition of Al2O3 nanoparticles generally weakened the cements. The ion release profile of the modified cements was the same in all cases. The addition of Al2O3, ZrO2 and TiO2 nanoparticles into GICs is beneficial, since it leads to reduction of the microscopic voids in the set cement. Of these, the use of ZrO2 and TiO2 nanoparticles also led to increased compressive strength. Nanoparticles did not release detectable levels of ions (Al, Zr or Ti), which makes them suitable for clinical use.