Inhibitors of corrosion 19 (1). Autoxidation studies on Fe2+-trimethylene-1,3-bisphosphonate as a model of a corrosion inhibiting surface layerThe autoxidation rate of Fe2+ salts depends on the pH value and is practically equal to zero at pH 2 and very high at pH 5-7. Addition of trimethylene-1,3-bis-phosphonic acid slows down autoxidation and gives rise to an increase in oxygen consumption; this resulting consumption is higher than might be explained by the stoichiometry of the Fe2+ oxidation. This fact may be explained by the oxidative conversion of trimethylene-1,3-bis-phosphonic acid to phosphoric acid with salts of trivalent iron being precipitated. These Fe3+-bis-phosphonates are precipitated in a tridimensional network; the Fe:P ratio is between 0.5 and 0.9 and the Fe:P ratio is between 0.5 and 0.9 and decreases as the pH of the system is decreased.
Notes:
Die Autoxidationsgeschwindigkeit der Fe2+. Salze ist stark abhängig vom pH und ist bei pH 2 praktisch gleich Null, bei pH 5-7 sehr hoch. Durch Zusatz von Trimethylen-1,3-bis-phosphonsäure wird die Autoxidation etwas verlangsamt und der Sauerstoffverbrauch stärker erhöht als es der Stöchiometrie der Fe2+-Oxidation entspricht. Dieser Umstand erklärt sich durch den oxidativen Abbau der Trimethylen-1,3-bis-phosphonsäure zu Phosphorsäure, wobei Salze des dreiwertigen Eisens als Niederschlag ausfallen. Diese Fe3+-bis-phosphonate sind dreidimensional vernetzt; das Fe:P-Verhältnis liegt zwischen 0.5 und 0.9 und wird mit abnehmendem pH-Wert geringer.
Additional Material:
3 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19760270402
Permalink