Keywords:
oxidation
;
film spalling
;
fayalite
;
internal oxidation
Source:
Springer Online Journal Archives 1860-2000
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Notes:
Abstract The oxidation behavior of Fe-14Cr-14Ni (wt.%) and of the same alloy with additions of 1 and 4% silicon was studied in air over the range of 900-1100° C. The presence of silicon completely changed the nature of the oxide scale formed during oxidation. The base alloy (no silicon) formed a thick outer scale of all three iron oxides and an internally oxidized zone of (Fe,Cr,Ni) spinels. The alloy containing 4% silicon formed an outer layer of Cr2O3 and an inner layer of either (or possibly both) SiO2 and Fe2SiO4. The formation of the iron oxides was completely suppressed. The oxidation rate of the 4% silicon alloy was about 200 times less than that of the base alloy, whereas the 1% silicon alloy exhibited a rate intermediate to the other two alloys. The actual ratio of the oxidation rates may be less than 200 due to possible weight losses by the oxidation of Cr2O3 to the gaseous phase CrO3. The lower oxidation rate of the 4% silicon alloy was attributed to the suppression of iron-oxide formation and the presence of Cr2O3, which is a much more protective scale.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF00611695
Permalink