The emulsion copolymerization of ethylene with hexafluoropropylene was studied by using 60Co γ-radiation as the initiator. The apparent rate of copolymerization is proportional to the 1.6 power of ethylene fugacity. The activation volume was calculated from the pressure dependence of the apparent rate constant of copolymerization and was -30 ml/mole, which is smaller than the value reported by Wada et al. for ethylene polymerization in tert-butyl alcohol. The copolymer produced had a broad composition from ethylene-rich to alternative. As expected, the former was a crystalline, polyethylenelike copolymer, but the latter was an amorphous and rubberlike copolymer. The glass transition temperature of the copolymers increased with an increase in hexafluoropropylene content. The thermal degradation temperature in an atmosphere of nitrogen decreased slightly with introduction of hexafluoropropylene in polyethylene, but the thermal degradation behavior in air was complicated by the introduction of hexafluoropropylene.
Additional Material:
13 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/pol.1974.170120313
Permalink