The mechanical properties of dense, hot-pressed ZrB 2 –30 vol% SiC ceramics were characterized from room temperature up to 1600°C in air. Specimens were tested as hot-pressed or after hot-pressing followed by heat treatment at 1400°C, 1500°C, 1600°C, or 1800°C for 10 h. Annealing at 1400°C resulted in the largest increases in flexure strengths at the highest test temperatures, with strengths of 470 MPa at 1400°C, 385 MPa at 1500°C, and 425 MPa at 1600°C, corresponding to increases of 7%, 8%, and 12% compared to as hot-pressed ZrB 2 –SiC tested at the same temperatures. Thermal treatment at 1500°C resulted in the largest increase in elastic modulus, with values of 270 GPa at 1400°C, 240 GPa at 1500°C, and 120 GPa at 1600°C, which were increases of 6%, 12%, and 18% compared to as hot-pressed ZrB 2 –SiC. Neither ZrB 2 grain size nor SiC cluster size changed for these heat-treatment temperatures. Microstructural analysis suggested additional phases may have formed during heat treatment and/or dislocation density may have changed. This study demonstrated that thermal annealing may be a useful method for improving the elevated temperature mechanical properties of ZrB 2 -based ceramics.
Print ISSN:
0002-7820
Electronic ISSN:
1551-2916
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics