In this study, ZnS powders with homogeneous morphology were synthesized using a colloidal processing method. Vacuum hot pressing was subsequently applied to consolidate the ZnS powders into infrared transparent ceramics (77.3% transmittance at wavelengths of 6.74 and 9.29 μm). The phase composition of the sintered ZnS suggests the presence of wurtzite as a minor phase in addition to the primary sphalerite phase, and microstructural analysis indicates that the ceramics are highly densified. It has been found that the VHP-sintered ZnS ceramics exhibit blue (450 nm) and green (530 nm) luminescence, which is due to the formation of zinc vacancies and sulfur interstitials, respectively, during the sintering process.