Publication Date:
2015-08-08
Description:
The flat surface of a Cu plate was processed by incremental frictional sliding at liquid nitrogen temperature. The surface treatment results in a hardened gradient surface layer as thick as 1 mm in the Cu plate, which contains a nanostructured layer on the top with a boundary spacing of the order of 100 nm. The boundary spacing increases with increasing distance from the surface, and is accompanied with a decrease in hardness from 2179?31MPa in the topmost surface layer to 568?10 MPa in the undeformed matrix.
Print ISSN:
1757-8981
Electronic ISSN:
1757-899X
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics