Recently, we reported on the retention of fine-grained micro-structure in Al2O3/3 vol% 3Y-ZrO2 composites using the pulse electric current sintering (PECS) technique. It was demonstrated that a high heating rate is beneficial for the retention of fine grains and homogeneous microstructure. As there are few reports on microstructural inhomogeneity and excessive grain growth in compacts densified by the PECS technique, we carried out a series of experiments on monolithic alumina by varying the sintering parameters and discussed the characteristic results. All specimens that were densified under selective sintering conditions attained high density (∼99% of the theoretical density) at 1250°3C in 〉 5 min. The average fracture strength of monolithic alumina was observed to be 741 ± 25 MPa and the fracture toughness was 2.2 MPa.m 〈1/2, and these were reasoned out to small grains. However, compacts sintered under very low compaction pressure attained ∼92%-93% of the theoretical density, and these specimens had undesirable microstructural inhomogeneity owing to differential sintering. Hence, in the present study, we address the problem of differential sintering.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1111/j.1551-2916.2004.00159.x