The effect of modification of polymer chains on crystal thickening during heating was investigated with an apparatus devised for rapid measurement of small-angle x-ray diffraction. Thickening of crystals still occurred even at a heating rate of 18°C/min in polyethylene irradiated with gamma ray doses of 30-300 Mrad, and the melting point was depressed. These results showed that the melting point depression due to irradiation is not due to a restriction on crystal thickening but rather to crystal lattice distortion. On the other hand, although methoxymethylation of nylon 6 completely inhibits crystal thickening, the melting point increases or decreases depending on the temperature of annealing preceding methoxymethylation. From these results we are led to conclude that irradiation and methoxymethylation are not effective means of obtaining the relation between melting point and crystal thickness.
Additional Material:
14 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/pol.1976.180140813