Description / Table of Contents:
In the present work oxygen index (OI) measurements and thermogravimetric analysis (TG) for a series of polyurethanes based on diols and isocyanate were conducted. It was found that a correlation exists between some of the thermal degradation parameters obtained from TG and OI-values. Analysis of experimental results confirms that the amount of mass loss at 250°C is directly proportional to the OI-value. It was also found that the logarithmic temperatures of maximal decomposition rates are directly proportional to the OI-values.
Notes:
In der vorliegenden Arbeit wurden für eine Serie von Polyurethanen auf der Basis von Diol und Isocyanat der Sauerstoffindex (SI) gemessen und die thermische Zersetzung mittels thermogravimetrischer Analyse (TG) untersucht. Dabei wurde ein Zusammenhang zwischen einigen Parametern der thermischen Zersetzung und den SI-Werten gefunden. Die Auswertung der experimentellen Ergebnisse zeigte, daß die Höhe des Massenverlustes bei 250°C und die SI-Werte direkt proportional zueinander sind. Derselbe Zusammenhang besteht auch zwischen dem Logarithmus der Temperatur bei der maximalen Zersetzungsgeschwindigkeit und den SI-Werten.
Additional Material:
5 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/apmc.1995.052240109