Time-of-flight neutron diffraction was used to study in-situ texture evolution and the α → β phase transformation in cold-drawn titanium upon continuous heating. The texture changes in the α phase at elevated temperatures upon recrystallization are presented. For the first time, a transient β texture was observed during the α → β transformation, as indicated by the initial rise and the final drop of the {110} β reflection intensity. This unusual observation is explained in terms of competitive growth between inter- and intragranular β allotriomorphs.
Similar content being viewed by others
References
F.A. Crossley: J. Aircraft, 1981, vol. 18, pp. 993–1002.
D. Eylon, S. Fujishiro, P.J. Postans, and F.H. Froes: J. Met., 1984, vol. 36, pp. 55–62.
M. Jackson and K. Dring: Mater. Sci. Technol., 2006, vol. 22, pp. 881–87.
T. Furuhara and T. Maki: Mater. Sci. Eng. A, 2001, vol. 312, pp. 145–54.
G.G.E. Seward, S. Celotto, D.J. Prior, J. Wheeler, and R.C. Pond: Acta Mater., 2004, vol. 52, pp. 821–32.
J.W. Elmer, J. Wong, and T. Ressler: Metall. Mater. Trans. A, 1998, vol. 29A, pp. 2761–73.
T. Grosdidier, Y. Combres, E. Gautier, and M.J. Philippe: Metall. Mater. Trans. A, 2000, vol. 31A, pp. 1095–1106.
S. Suwas and A.K. Singh: Metall. Mater. Trans. A, 2004, vol. 35A, pp. 925–38.
J. Romero, A. Preuss, and J.Q. da Fonseca: Acta Mater., 2009, vol. 57, pp. 5501–11.
J. Romero, M. Preuss, and J.Q. da Fonseca: Scripta Mater., 2009, vol. 61, pp. 399–402.
H.R. Wenk, I. Lonardelli, and D. Williams: Acta Mater., 2004, vol. 52, pp. 1899–907.
I. Lonardelli, N. Gey, H.R. Wenk, M. Humbert, S.C. Vogel, and L. Lutterotti: Acta Mater., 2007, vol. 55, pp. 5718–27.
D. Phelan, M. Reid, N. Stanford, and R. Dippenaar: JOM, 2006, vol. 58, pp. 67–69.
R. Riedel: “Spallation Neutron Source Data Acquisition System,” SNS Report No. 107030200-TD005-R04, Oak Ridge National Laboratory, Oak Ridge, TN, 2007.
X.L. Wang, T.M. Holden, G.Q. Rennich, A.D. Stoica, P.K. Liaw, H. Choo, and C.R. Hubbard: Physica B, 2006, vol. 385, pp. 673–75.
X.L. Wang and A.D. Stoica: Nucl. Instrum. Meth., 2009, vol. 600, pp. 309–12.
K. An, X.-L. Wang, and A.D. Stoica: unpublished work. Oak Ridge National Laboratory, Oak Ridge, TN, 2010. http://www.ornl.gov/~k6e/VDRIVE/.
W.G. Burgers: Physica, 1934, vol. 1, pp. 561–86.
A.C. Larson and R.B. Von Dreele: “General Structure Analysis System (GSAS),” Los Alamos National Laboratory Report LAUR, Los Alamos National Laboratory, Los Alamos, NM, 2004, pp. 86–748.
The authors thank A. Church, J. Carmichael, L. Walker and L.J. Santodonato for their technical support for commissioning the ILL vacuum furnace. The neutron scattering work was carried out at the Spallation Neutron Source (SNS), which is operated with the support from the Division of Scientific User Facilities, Office of Basic Energy Sciences, US Department of Energy, under contract DE-AC05-00OR22725 with UT-Battelle, LLC. H.B. was supported by the Division of Materials Sciences and Engineering, Basic Energy Sciences. US Department of Energy.
Author information
Authors and Affiliations
Corresponding author
Additional information
Manuscript submitted December 10, 2010.
Rights and permissions
About this article
Cite this article
Ma, D., Stoica, A.D., An, K. et al. Texture Evolution and Phase Transformation in Titanium Investigated by In-Situ Neutron Diffraction. Metall Mater Trans A 42, 1444–1448 (2011). https://doi.org/10.1007/s11661-011-0667-2
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11661-011-0667-2