Summary
Poly(styrene)-block-poly(ethyleneoxide), abbreviated as (PS-b-PEO) were used as emulsifiers in emulsion polymerization of styrene and methyl methacrylate. The block copolymers had a poly(styrene) block with Mn=1000 g/mol and a poly(ethyleneoxide) block with Mn=1000, 3000 or 5000 g/mol, respectively. Stable dispersions were obtained when the PEO block molecular weight was higher than 1000 g/mol. Also the amphiphilic properties of the copolymers depended on the PEO chain length. Block copolymer micelles with hydrodynamic radii between 11 and 17nm were observed. Emulsion polymerization was performed at different block copolymer concentration at 60 and 80°C. Particle size varied between 50 and 300nm and decreased with increasing copolymer concentration. The particle size was larger at higher temperature, but the size distribution was narrower. Polymerization of methyl methacrylate gave smaller particles when compared to styrene. The dispersions were very stable towards high electrolyte concentration, but flocculation occurred at elevated temperatures. Both observations indicate that the dispersions are sterically stabilized.
Similar content being viewed by others
References
Napper DH (1983) Polymeric Stabilization of Colloidal Dispersions, Academic Press, New York
Lyklema J (1991) Fundamentals of Interface and Colloid Science, Academic Press, London
Jialanella GJ, Firer EM, Piirma I (1992) J Polym Sci Part A: Polym Chem 30: 1925
Bahadur P, Riess G (1991) Tenside Surf Det 28: 173
Riess G (1993) Makromol Chem Macromol Symp 69: 125
Fock J Goldschmidt AG Ger Offen DE 4134967
Tauer K, Goebel K-H, Kosmella S, Stähler K, Neelson J (1990) Makromol Chem Macromol Symp 31: 107
Xu R, Winnik MA, Hallett FR, Riess G, Croucher MD (1991) Macromolecules 24: 87
Dunn AS (1992) in: Polymer Latexes, ACS Symp Ser. 492: 45
Schechtman LA (1992) in: Polymer Solutions, Blends and Interfaces, Noda I, Rubingh DN (eds), Elsevier, Amsterdam
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Berger, M., Richtering, W. & Mülhaupt, R. Use of poly(styrene)-block-poly(ethyleneoxide) as emulsifier in emulsion polymerization. Polymer Bulletin 33, 521–528 (1994). https://doi.org/10.1007/BF00296159
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00296159