Hydrogen-induced embrittlement of fine-grained twin-roll cast AZ31 in distilled water and NaCl solutions

  • Original Paper
  • Published:
Journal of Materials Science Aims and scope Submit manuscript

Abstract

Twin-roll cast magnesium has a fine-grained microstructure and exhibits relatively high strength and ductility. However, hydrogen-induced embrittlement in magnesium alloys can limit the mechanical properties substantially and can lead to sudden and unpredictable failure. In this study, embrittlement is determined by means of slow strain rate tests (SSRT) and instrumental indentation tests (IIT). The latter enables analysis of embrittlement under the suppression of crack propagation mechanisms and surface influences (e.g. notch effects due to pitting) and is a new technique for the investigation of hydrogen embrittlement (HE). In this study, the influence of immersion time and elastic deformation on the HE of twin-roll cast and heat-treated magnesium sheets (AZ31) was analysed. Distilled water and two NaCl solutions (0.05 and 0.5 wt%) served as analysing media. It is shown that both influencing factors significantly affect the rate and the degree of HE. Relatively short immersion in distilled water led to a substantial decrease in strain and an increase in brittleness, even without external mechanical loading. In contrast, strength was not affected by immersion in water and the resulting HE. In comparison to immersion in distilled water, immersion in sodium chloride solution led to a total loss of plasticity and a decrease in strength during SSRT without a distinct increase in embrittlement during IIT. Analysis by X-ray diffractometry did not determine a detectable amount of magnesium hydrides in the embrittled AZ31 structure.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13
Fig. 14
Fig. 15

Similar content being viewed by others

References

  1. Stampella RS, Procter RPM, Ashworth V (1984) Environmentally-induced cracking of magnesium. Corros Sci 24:325–337

    Article  Google Scholar 

  2. Winzer N, Atrens A, Song G, Ghali E, Dietzel W, Kainer KU, Hort N, Blawert C (2005) A critical review of stress corrosion cracking (SCC) of magnesium alloys. Adv Eng Mater 7:659–693

    Article  Google Scholar 

  3. Zeng RC, Zhang J, Huang WJ, Dietzel W, Kainer KU, Blawert C, Wei K (2006) Review of studies on corrosion of magnesium alloys. Trans Nonferr Met Soc China 16:763–771

    Article  Google Scholar 

  4. Argade GR, Yuan W, Kandasamy K, Mishra RS (2012) Stress corrosion cracking susceptibility of ultrafine grained AZ31. J Mater Sci 74:6812–6822. doi:10.1016/j.corsci.2005.02.017

    Article  Google Scholar 

  5. Winzer N, Atrens A, Dietzel W, Raja V, Song G, Kainer KU (2008) Characterisation of stress corrosion cracking (SCC) of MgAl alloys. Mater Sci Eng 488:339–351

    Article  Google Scholar 

  6. Winzer N, Atrens A, Dietzel W, Song G, Kainer KU (2008) Fractography of stress corrosion cracking of MgAl alloys. Metall Mater Trans A 39A:1157–1173

    Article  Google Scholar 

  7. Winzer N, Atrens A, Dietzel W, Song G, Kainer KU (2007) Stress corrosion cracking in magnesium alloys: characterization and prevention. JOM 59(8):49–53

    Article  Google Scholar 

  8. Lynch S (2012) Hydrogen embrittlement phenomena and mechanisms. Corros Rev 30:105–123

    Google Scholar 

  9. Lynch S (2012) Mechanistic and fractographic aspects of stress corrosion cracking. Corros Rev 30:63–104

    Google Scholar 

  10. Kannan MB, Dietzel W, Zeng R, Zettler R, dos Santos JF (2007) A study on the SCC susceptibility of friction stir welded AZ31 Mg sheets. Mater Sci Eng A 460–461:243–250

    Article  Google Scholar 

  11. Song RG, Blawert C, Dietzel W, Atrens A (2005) A study on stress corrosion cracking and hydrogen embrittlement of AZ31 magnesium alloy. Mater Sci Eng A 399:308–317

    Article  Google Scholar 

  12. Yao X, Zhu ZH, Cheng HM, Lu GQ (2008) Hydrogen diffusion and effect of grain size on hydrogenation kinetics in magnesium hydrides. J Mater Res 23:336–340

    Article  Google Scholar 

  13. Fairman L, West J (1965) Stress corrosion cracking of a magnesium aluminium alloy. Corros Sci 5:711–716

    Article  Google Scholar 

  14. Fairman L, Bray HJ (1971) Intergranular stress corrosion cracking propagation in magnesium alloys. Br Corros J 6:170–174

    Article  Google Scholar 

  15. Schimmel H, Kearley G, Huot J, Mulder F (2005) Hydrogen diffusion in magnesium metal (alpha phase) studied by ab initio computer simulations. J Alloy Compd 404–406:235–237

    Article  Google Scholar 

  16. Nishimura C, Komaki M, Amano M (1999) Hydrogen permeation through magnesium. J Alloy Compd 329:293–295

    Google Scholar 

  17. Kannan MB, Dietzel W, Blawert C, Atrens A, Lyon P (2008) Stress corrosion cracking of rare-earth containing magnesium alloys ZE41, QE22 and Elektron 21 (EV31A) compared with AZ80. Mater Sci Eng A 480:529–539

    Article  Google Scholar 

  18. Chen J, Wang J, Han E, Ke W (2008) Effect of hydrogen on stress corrosion cracking of magnesium alloy in 0.1 M Na2SO4 solution. Mater Sci Eng A 488:428–434

    Article  Google Scholar 

  19. Chen J, Ai M, Wang J, Han E, Ke W (2009) Stress corrosion cracking behaviors of AZ91 magnesium alloy in deicer solutions using constant load. Mater Sci Eng A 515:79–84

    Article  Google Scholar 

  20. Nozaki T, Hanaki S, Yamashita M, Uchida H (2003) Proceedings of 13th Asian-Pacific Corrosion Control Conference, Osaka, K15

  21. DIN EN ISO 14577-1 Metallic materials-Instrumented indentation test for hardness and material parameters-Part 1 Test method (ISO/DIS 14577-1:2012), Beuth Verlag GmbH, 2012

  22. Janakiraman N, Aldinger F (2010) Indentation analysis of elastic and plastic deformation of precursor-derived Si–C–N ceramics. J Eur Ceram Soc 30:775–785

    Article  Google Scholar 

  23. Abidin NIZ, Martin D, Atrens A (2011) Magnesium corrosion in different solutions. Mater Sci Forum 690:369–372

    Article  Google Scholar 

  24. Moriwaki T, Akahama Y, Kawamura H, Nakano S, Takemura K (2006) Structural phase transition of rutile-type MgH2 at high pressures. J Phys Soc Jpn 75:074603

    Article  Google Scholar 

  25. Shi Z, Atrens A (2011) An innovative specimen for Mg corrosion studies. Mater Sci Forum 690:365–368

    Article  Google Scholar 

  26. Ebtehaj K, Hardie D, Parkins RN (1988) The influence of chloride-chromate solution composition on the stress corrosion cracking of a MgAl alloy. Corros Sci 28:811–821

    Article  Google Scholar 

Download references

Acknowledgements

The authors thank the Saxon State Ministry for Economic Affairs, Labour and Transport, the Development Bank of Saxony, in particular, as well as the European Social Fund for their financial support of the project 080943441.

Conflict of interest

The authors declare that they have no conflict of interest.

Author information

Authors and Affiliations

  1. Institute of Materials Engineering, TU Bergakademie Freiberg, Gustav-Zeuner-Str. 5, 09599, Freiberg, Germany

    F. Tuchscheerer & L. Krüger

Authors
  1. F. Tuchscheerer
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. L. Krüger
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to F. Tuchscheerer.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Tuchscheerer, F., Krüger, L. Hydrogen-induced embrittlement of fine-grained twin-roll cast AZ31 in distilled water and NaCl solutions. J Mater Sci 50, 5104–5113 (2015). https://doi.org/10.1007/s10853-015-9064-3

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10853-015-9064-3

Keywords

Search

Navigation