The influence of Co additions on the sintering of nickel oxide was studied. On the basis of the density, specific surface area and Me3+ ion concentration changes, in the Co y Ni1−y O samples, having 0, 1, 5 and 10 cation % of Co, a positive effect of Co ions on the densification was assumed, during sintering at 500 to 900° C in an argon atmosphere. Using special heat-treatment, the differences in specific surface area of the investigated powders were eliminated. The differences in green densities were excluded as well and from the results, it was possible to show that dissolved Co ions enhance nickel oxide densification process.
Similar content being viewed by others
References
S. Bošković and M. Stevanović, Conference on Ceramic for Electronics, Liblice Cssr, April, (1947), proceedings, paper No. 22.
Idem, Conference on modern Inorganic materials, Ljubljana, Yugoslavia, September 1974.
A. G. Chervinko, P.M. Melnik and S. S. Lisnak, Thesis Dokl. IImezh. Sov. po metodami poluchenia i analyza ferritovih materialov, Doneck, 1962, p. 62.
S. Bosković and B. Zivanović, J. Mater. Sci. 9 (1974) 117.
D. L. Johnson and I. B. Cutler, in “Phase Diagrams”, Vol. 2, edited by A. M. Alper, (Academic Press, New York, 1970) p. 265.
F. Kröger, in “Sintering and Related Phenomena”, edited by G. C. Kuczynski (Gordon and Breach, New York, 1963) p. 29.
J. J. Stiglich, D. H. Whitmore and J. B. Cohen, J. Amer. Ceram. Soc. 56 (1973) 119.
K. Weiss, Ber. Dt. Keram. Gess. 48 (1971) 489.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Bošković, S., Stevanović, M. Sintering of cobalt-doped nickel oxide. J Mater Sci 10, 25–31 (1975). https://doi.org/10.1007/BF00541028
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00541028