Abstract
Sol gel derived composite materials were prepared from methacryloxypropyltrimethoxysilane (MPTS) and tetraethyleneoxidedimethacrylate (TEGDMA). The amount of MPTS in the composites was varied from 0 to 50 mole%. MPTS was prehydrolyzed at room temperature with 0,1 mole/l HCl/H2O. After complete removal of solvent calculated amounts of TEGDMA were added to the reaction mixture of the prehydrolyzed MPTS. Thermically initiated free radical copolymerization of the methacrylate endgroups was performed in the resulting mixture under nitrogen atmosphere using azobisisobutyronitril (AIBN) as initiator. The composites were investigated by high resolution transmission electronmicroscopy in order to investigate the morphology. The thermomechanical properties as storage, loss modulus, tan δ as well as the glass transition temperature (T g ) of the composites were estimated by dynamic mechanical thermal analysis (DMTA).
Similar content being viewed by others
References
H. Schmidt, J. Non-Cryst. Solids 73, 681 (1985).
L. Kador, D. Haarer, R. Fischer, R. Kasemann, S. Brück, H. Schmidt, and H. Dürr, Adv. Mater. 5, 270 (1993).
L. Delattre, C. Dupuy, and F. Babonneau, Proc. First European Workshop on Hybrid Organic-Inorganic Materials, Chateau de Bierville, France, edited by C. Sanchez and R. Ribot (Uversité Pierre et Marie Curie, Paris, 1993), pp. 185–188.
C.J.T. Landry, B.K. Coltrain, and B.K. Brady, Polymer 33, 1486 (1992).
Rights and permissions
About this article
Cite this article
Becker, C., Krug, H. & Schmidt, H. Mechanical Properties of Copolymers from Methacrylate Functionalized Silanes and Bifunctional Methacrylate Monomers. Journal of Sol-Gel Science and Technology 8, 625–627 (1997). https://doi.org/10.1023/A:1018364024805
Issue Date:
DOI: https://doi.org/10.1023/A:1018364024805