Vol. 551-552 (July 2007), p. 249-254
ISSN:
1662-9752
Quelle:
Scientific.Net: Materials Science & Technology / Trans Tech Publications Archiv 1984-2008
Thema:
Maschinenbau
Notizen:
In this paper, an ultra-fine grained AZ31 magnesium alloy sheet with grain size less than3μm was generated by three-run accumulative roll bonding of as cast alloy at a deformationtemperature of 350°C and a reduction of 80% for each pass. The microstructures on the different ARBstages were observed and superplasticity examination in the ultrafine grained AZ31 alloy were carriedout at a fixed temperature of 300°C and varied strain rate ranging from 10-4 to 10-1 s-1. It is indicatedthat significant grain refinement was mainly achieved in the first run and gradual uniformity of grainsize in the next by continuous dynamic recrystalization. Besides, a superplastic deformation with amoderate elongation-to-fracture of 316% was obtained at a strain rate of 10-2 s-1 indicating a lowtemperature and high strain rate superplasticity, while a maximum elongation-to-fracture of 562%at10-4 s-1. The strain rate sensitivity exponent as high as of 0.34-0.41 implies the dominant role ofgrain boundary sliding in superplastic deformation at strain rate ranging from 10-3 to 10-2 s-1. Theresults indicate a possible approach to produce magnesium alloy sheet with fine grain and excellentdeep drawing workability
Materialart:
Digitale Medien
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/02/16/transtech_doi~10.4028%252Fwww.scientific.net%252FMSF.551-552.249.pdf
Permalink
|
Standort |
Signatur |
Erwartet |
Verfügbarkeit |