Publication Date:
2013-04-02
Description:
Yttria partially stabilized zirconia Y-PSZ/glass-ceramic composites were prepared by reaction sintering using powder mixtures of a SiO 2 – Al 2 O 3 – ZnO – CaO – ZrO 2 – TiO 2 -based glass and yttria partially stabilized zirconia (Y-PSZ). The glass crystallized during sintering at temperatures of 1173, 1273, and 1373 K to give a glass-ceramic matrix for high-temperature protecting coatings. With the increasing firing time, the added zirconia reacted with the base glass and a glass-ceramic material with dispersed zircon particles was prepared in situ . Furthermore, the added zirconia changed the crystallization behavior of the base glass, affecting the shape, amount, and distribution of zircon in the microstructure. The bipyramid-like zircon grains with imbedded residual zirconia particles turned out to have two growth mechanisms: the inward growth and the outward growth, and its rapid growth was mainly dominated by the later one. For comparison, the referenced glass-ceramic was prepared by sintering using exclusive glass granules and its crystallization behavior at 1173–1373 K was examined as well. Scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), transmission electron microscopy (TEM), and X-ray diffraction (XRD) were used to characterize the crystallization behavior of the base glass and the phase evolution of the Y-PSZ/glass-ceramic composites.
Print ISSN:
0002-7820
Electronic ISSN:
1551-2916
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Permalink