Description / Table of Contents:
After comparison of three catalyst systems, i.e. [Nd(Oct)3/Al2Cl3ET3/Al(i-But)3, Ni(Oct)2/BF3OEt2/AlEt3 and Al(i-But)3/I2/TiCl4] the titanium catalyst system was used for the copolymerization of 1,3-butadiene with propylene oxide. The effects of monomer ratio on copolymer composition, conversion, microstructure, molar mass and molar mass distribution as well as of time of polymerization and of the aluminium/titanium ratio were evaluted. The copolymerization parameters were determined according to Kelen-Tüdős as rbutadiene = 0,9 and rpropylene oxide = 3,9. Copolymerization was confirmed by 13C NMR spectroscopy and extract evaluation combined with 1H NMR spectroscopy.
Notes:
Für die Copolymerisation von 1,3-Butadien mit Propylenoxid wurde nach dem Vergleich der drei Katalysatorsysteme Nd(Oct)3/Al2Cl3ET3/Al(i-But)3, Ni(Oct)2/ BF3OEt2/AlEt3 und Al(i-But)3/I2/TiCl4 das Titankatalysatorsystem eingesetzt. Neben dem Einfluß der Monomerzusammensetzung auf den Umsatz, die Microstruktur, die Copolymerzusammensetzung, die Molmassen sowie die Molmassenverteilungen wurden auch die Polymerisationszeit und das Aluminium/Titan-Verhältnis untersucht. Die Copolymerisationsparameter wurden nach Kelen-Tüdős zu rButadien = 0,9 und rPropylenoxid = 3,9 bestimmt. Der Copolymernachweis erfolgte über 13C-NMR-Spektroskopie und Extraktionsuntersuchungen in Verbindung mit 1H-NMR-Spektroskopie.
Additional Material:
8 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/apmc.1996.052390110
Permalink