Publication Date:
2019-03-11
Description:
Nitrogen-doped lithium niobate (LiNbO3:N) thin films were successfully fabricated on a Si-substrate using a nitrogen plasma beam supplied through a radio-frequency plasma apparatus as a dopant source via a pulsed laser deposition (PLD). The films were then characterized using X-Ray Diffraction (XRD) as polycrystalline with the predominant orientations of (012) and (104). The perfect surface appearance of the film was investigated by atomic force microscopy and Hall-effect measurements revealed a rare p-type conductivity in the LiNbO3:N thin film. The hole concentration was 7.31 × 1015 cm−3 with a field-effect mobility of 266 cm2V−1s−1. X-ray Photoelectron Spectroscopy (XPS) indicated that the atom content of nitrogen was 0.87%; N atoms were probably substituted for O sites, which contributed to the p-type conductivity. The realization of p-type LiNbO3:N thin films grown on the Si substrate lead to improvements in the manufacturing of novel optoelectronic devices.
Electronic ISSN:
1996-1944
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Permalink