Publication Date:
2020-10-29
Description:
A non-equiatomic refractory high entropy alloy (RHEA), (W35Ta35Mo15Nb15)95Ni5 with high density of 14.55 g/cm3 was fabricated by powder metallurgical process of mechanical alloying (MA) and spark plasma sintering (SPS). The mechanical alloying behavior of the metallic powders was studied systematically, and the microstructure and phase composition for both the powders and alloys were analyzed. Results show that the crystal consists of the primary solid solution and marginal oxide inclusion (Nb5.7Ni4Ta2.3O2). In addition, the maximum strength, yield strength and fracture strain are, 2562 MPa, 2128 MPa, 8.16%, respectively.